8mm clear tempered toughened reinforced building glass

Characteristic of 8mm clear tempered glass

For more information, please visit Northglass.

1.safety

When the glass is damaged by an external force, the debris will become a honeycomb-like obtuse-angled small particle, which is not easy to cause serious damage to the human body.

2.high strength

The impact strength of an 8mm tempered glass of the same thickness is 3 to 5 times that of ordinary glass, and the bending strength is 3 to 5 times that of ordinary glass.

3.Thermal stability

8mm tempered glass has good thermal stability, and can withstand a temperature difference of three times that of ordinary glass, and can withstand a temperature difference of 300 °C.

4.advantage

1. The first is that the strength is several times higher than that of ordinary glass and it is resistant to bending.

2. The second is safe use, and its load-bearing capacity is improved to improve the fragile nature. Even if the 8mm tempered glass is broken, it is a small piece with no sharp angle, and the damage to the human body is greatly reduced. 

3. The quenching and rapid heat properties of 8mm tempered glass are 3 to 5 times higher than that of ordinary glass and generally can withstand temperature changes of more than 250 degrees, which has obvious effects on preventing thermal cracking. It is one of the safety glasses. To ensure the safety of qualified materials for high-rise buildings.

Disadvantages of 8mm tempered glass:

1. The 8mm tempered glass can no longer be cut and processed, and the glass can only be processed to the required shape before tempering, and then tempered.

2. Although the strength of 8mm tempered glass is stronger than that of ordinary glass, 8mm tempered glass has the possibility of self-explosion (self-rupture), while ordinary glass does not have the possibility of self-explosion.

Want more information on toughened glass 8mm? Feel free to contact us.

3. The surface of the 8mm tempered glass will have unevenness (wind spots) and a slight thickness will become thin. The reason for the thinning is that after the glass is melted by hot melt, it is rapidly cooled by a strong wind force so that the internal crystal gap of the glass becomes small and the pressure becomes large, so the glass is thinner after tempering than before tempering. Under normal circumstances, the glass of 4~6mm is thinned by 0.2~0.8mm after tempering, and the glass of 8~20mm is thinned by 0.9~1.8mm after tempering. The degree of specificity depends on the equipment, which is why 8mm tempered glass cannot be mirrored.

4. The flat glass used for construction after passing through the tempering furnace (physical tempering) is generally deformed, and the degree of deformation is determined by the process of equipment and technicians. To a certain extent, it affects the decorative effect (except for special needs).

Production

8mm tempered glass is obtained by first cutting the ordinary annealed glass into the required size and then heating it to about 700 degrees near the softening point, and then performing rapid and uniform cooling (usually 5-6MM glass is heated at 700 °C for 240 seconds). Cool down for about 150 seconds. 8-10MM glass is heated at 700 °C for about 500 seconds, and the temperature is lowered by about 300 seconds. In short, depending on the thickness of the glass, the time for heating and cooling is different. After the tempering treatment, the surface of the glass forms uniform compressive stress, while the inside forms tensile stress, which improves the bending and impact strength of the glass, and its strength is about four times that of the ordinary annealed glass. The 8mm tempered glass that has been tempered can no longer be processed or damaged by any cutting, grinding, etc., otherwise, it will &#;break the bones&#; due to the failure of the uniform compressive stress.

if you want to know more information about the BTG glass company, please click the link as below:

https://www.better-glass.com/news-events/

Description

Buy Glass 8mm Toughened glass is 4 to 5 times stronger than annealed glass of the same 8mm thickness and is best designed for the most important applications for protection.

Because of its increased strength, Toughened Glass allows architects and builders far greater scope in their use of glass in buildings.

8mm Toughened glass is produced to BS EN , the product is a a soda lime silicate glass intended to be used in buildings and construction work.

8mm Toughened Glass is manufactured by subjecting cut to size panes of glass to a heating and cooling treatment whereby high compressive stresses are set up at the surfaces with balancing tensile stresses in the centre.

The high compressive surface stresses give the glass its increased strength i.e toughened glass.

When / if broken 8mm toughened glass will break into lots of small usually blunt pieces making it much safer than annealed (untoughened) glass which breaks in to large usual sharp pieces.

What are the uses for Toughened Glass?

• Facade Glass
• Glass Doors
• Architectural Glazing
• Handrails & Balustrade Glass
• Lifts & Elevator Glass
• Shelves
• Shop Windows
• Skylights
• Kitchen Splashback Glass
• Pool Surround Glass
• Partitioning Glass
• Table Top Glass
• Shelve Glass
• Aquarium Glass

You, the specifier, are responsible for checking with building control and/or other regulatory bodies to ensure that 8mm Toughened and the fitting are suitable for your specific project. We are a supply only company.

If you want to learn more, please visit our website tempered float glass.